Zirconia Orodent Gold 1200 MPa

Zirconia Gold is the golden effect of a natural smile, this zirconia avoids the unnatural effect of white during prosthesis retouching. The material composition is designed to have extremely high flexural strength and at the same time excellent translucency.

Description

Full description

ZIRCONIA with a NATURAL BASE similar to A1 and a high flexural strength (1200 MPa) for crowns and anatomical bridges for up to 12 units. It’s ideal because the white effect will never appear during retouching.

Diameter: Ø: 98 mm
Available heights: 10 mm to 25 mm
Indications: suitable for extremely natural results.
Missing elements: max 2
Disc colour: NATURAL, ≈ A1
Colouring recommendations: Immersion technique for 20 seconds or Brush Technique* with COLORODENT GOLD and COLORODENT SUPERCOLORS
Aging: for life thanks to the new generation Tosoh powders

Technical Specifications

Sintering instructions

Sintering of Resistance Furnace

Maximum thickness of works <7mm (as a reference take the maximum thickest element of the work)

Step	Temperature	Gradient °C/min	Holding time	Duration	Total time
0	30°C	-	-	-
1	930°C	9°C	30 min	130 min
2	1530°C	2.4°C	120 min	370 min
3	100°C	-9.0°C	0 min	160 min
Total: 660 min					h 11

! Oven opening temperature: <100°C

Maximum thickness of the works >7mm (as a reference take the maximum thickest element of the work)

Step	Temperature	Gradient °C/min	Holding time	Duration	Total time
0	30°C	-	-	-
1	930°C	9°C	30 min	130 min
2	1530°C	1.8°C	120 min	453 min
3	100°C	-9.0°C	0 min	160 min
Total: 743 min					h 12.4

! Oven opening temperature: <100°C

Technical and Safety Data Sheets

Download the Technical Data Sheet

Download the Safety Data Sheet

Additional information

Resistenza alla flessione	1200 MPa
Traslucenza	45%
Tipi di lavoro	Single crowns, reduced bridges, full bridges up to 12 units (Toronto bridge)
Sinterizzazione	1530 °C
Liquidi coloranti	Gold
Tipologia	Monolayer